Search Results

The performance characteristics of a commercial lean-NOX trap catalyst were evaluated between 200 and 500°C, using H2, CO, and a mixture of both H2 and CO as reductants before and after different high-temperature aging steps, from 600 to 750°C. Tests included NOX reduction efficiency during cycling, NOX storage capacity (NSC), oxygen storage capacity (OSC), and water-gas-shift (WGS) and NO oxidation reaction extents. The WGS reaction extent at 200 and 300°C was negatively affected by thermal degradation, but at 400 and 500°C no significant change was observed. Changes in the extent of NO oxidation did not show a consistent trend as a function of thermal degradation. The total NSC was tested at 200, 350 and 500°C. Little change was observed at 500°C with thermal degradation but a steady decrease was observed at 350°C as the thermal degradation temperature was increased.

Regeneration of diesel particulate filters poses major challenges in developing the particulate matter emission control technology to meet EPA 2007/2010 emissions regulations. The problem areas are multifold due to the complexity involved in designing the filter system, developing regeneration strategies and controlling the regeneration process. This paper discusses the need for active regeneration systems. It also addresses several key limitations and trade-offs between the regeneration strategy, chemical kinetics, exhaust gas temperature and the regeneration efficiency. Passive regeneration of diesel particulate filter systems is known to be highly dependent on the engine-out [NOx/PM] ratio as well as exhaust temperature over the duty cycle. Using catalytic oxidation of auxiliary fuel injected into the system, the exhaust gas temperature can be successfully enhanced for filter regeneration.

Several complementary experimental techniques were applied to investigate kinetics of diesel soot oxidation by O2 in an attempt to provide accurate data for modeling of the Diesel Particulate Filters regeneration process. For two diesel soot samples with measurably different properties, it was shown that the complexity of their overall kinetic behavior was due to an initial period of rapidly changing reactivity. This initial high reactivity was understood not to be related to the SOF, and was quantitatively correlated to the extent of soot pre-oxidation. This initial reactivity can affect the averaged apparent kinetic parameters, for example resulting in the lower apparent activation energy values. After the initial soot pre-oxidation, which consumed ∼10-25% of carbon, the remaining soot was behaving very uniformly, producing linear Arrhenius plots in a remarkably broad range of temperatures (330-610°C) and integral conversions (up to 90%).

Advanced flow-reactor capabilities created at Cummins were applied to the study of the diesel particulate matter (soot) oxidation process. This approach complemented the on-engine studies with a number of important features, including accurate control of gas composition and soot layer temperature. Using the developed methodology for quantitative soot oxidation studies in a broad range of temperatures (200-700°C), an initial set of experiments was performed to compare the behavior of the real and model soot samples under the identical conditions (10%vol. of O2, 0-15%vol. of H2O). It was found that presence of H2O vapor synergistically enhances the rate of oxidation by O2 of the diesel soot sample. However, the behavior of the model soot sample (carbon black) was virtually not affected by H2O. Kinetic analysis of the obtained results revealed an unusual type of behavior, with the activation energy of soot oxidation increasing in the course of the experiment.